Pyramid™ (PEEK)

The Pyramid™ polymers are Polymics’ premier line up of high-performance materials for use in a variety of industries.

Pyramid™ Polymers

The Pyramid™ polymers are Polymics’ premier line up of high-performance materials for use in a variety of industries, including Energy (Oil & Gas), Electronics (Semiconductor), Medical (OrthoPEEK®), Industrial, and others.

Universal Pyramid™ Polymer Properties

Pyramid Polymers

Excellent performance at high temperatures

maintain physical and mechanical properties even during exposure to a wide range of temperatures
Pyramid Polymers

Excellent chemical resistance

in environments that are corrosive, high temperature, and/or high pressure
Pyramid Polymers

High mechanical strength,

stiffness, creep resistance, and fatigue properties
Pyramid Polymers

High wear resistance

due to low coefficient of friction
Pyramid Polymers

Excellent hydrolysis resistance

in steam, water, and brine environments; in addition to low moisture absorption and low permeability
Pyramid Polymers

Natural flame retardant composition

and electrical properties that remain stable over a wide range of frequencies and temperatures
Pyramid Polymers

Recyclable,

benefitting both the environment and company regulation standards

Standard Pyramid™ Compounds

Please note that while the materials shown below are the standard commercial products offered by Polymics, Ltd., Polymics has the experience and capability to compound custom materials from a wider range of thermoplastic resins and fillers. Please contact us with any questions or inquiries you may have for materials not shown here.

PEEK (Polyetheretherketone)

PEKK (Polyetherketoneketone)

Pyramid Polymers

Unfilled High Flow Virgin PEEK

Pyramid Polymers

Unfilled Extrusion Grade Virgin PEEK

Pyramid Polymers

Unfilled Reprocessed, High Flow Grade PEEK

Pyramid Polymers

Unfilled Reprocessed, Extrusion Grade PEEK

Pyramid Polymers

30% Glass Fiber PEEK

Pyramid Polymers

30% Carbon Fiber PEEK

Pyramid Polymers

Wear Grade PEEK

Pyramid Polymers

Pyramid™ CC

Highly Reinforced, Randomly Oriented, Long Carbon Fiber PEEK
Pyramid Polymers

Unfilled Amorphous PEKK

Pyramid Polymers

Unfilled Crystalline PEKK

Pyramid Polymers

PTFE-Lubricated Crystalline PEKK

Pyramid Polymers

Very Low Coefficient of Friction PTFE-Lubricated Crystalline PEKK

Pyramid Polymers

30% Glass Fiber Crystalline PEKK

Pyramid Polymers

30% Carbon Fiber Crystalline PEKK

Pyramid Polymers

Wear Grade Crystalline PEKK

PEKK Plus® (PEKK/PEI Blends)

Ultem® PEI (Polyetherimide)

Pyramid Polymers

Unfilled PEKK Plus®

Pyramid Polymers

30% Glass Fiber PEKK Plus®

Pyramid Polymers

30% Carbon Fiber PEKK Plus®

Pyramid Polymers

Wear Grade PEKK Plus®

Pyramid Polymers

Unfilled, Extrusion Grade Virgin PEI

Pyramid Polymers

Unfilled Reprocessed, Extrusion Grade PEI

Pyramid Polymers

30% Glass Fiber PEI

Pyramid Polymers

30% Carbon Fiber PEI

Pyramid Polymers

Electro-Static Dissipative (ESD) PEI

PPS (Polyphenylene Sulfide)

PPSU (Polyphenylsulfone)

Pyramid Polymers

Unfilled PPS

Pyramid Polymers

40% Glass-Filled PPS

Pyramid Polymers

30% Carbon Fiber PPS

Pyramid Polymers

PTFE-Lubricated PPS

Pyramid Polymers

Wear Grade PPS

Pyramid Polymers

30% Carbon Fiber PPSU

  1. All grades also available in black
  2. PEI with glass filler levels from 5% to 40% is also available as a standard
  3. PEI is commonly referred to by the trade name Ultem®

The Pyramid™ CC Product Line

High Strength Composite and Hybrid material

Pyramid CC consists of four basic high strength PEEK/carbon fiber composite systems. The basic technical differentiation is that these are PEEK resin matrix filled with various type of carbon fiber reinforcement.

1. Pyramid CC100 is chopped carbon fiber (1/4” or so to 1/2”) reinforced, feed material can be in fiber bundles, chopped tapes or other irregular chopped fiber forms. Typically used as reinforced structural components such as medical instruments.

2. Pyramid CC200 is continuous carbon fiber reinforced, feed material is woven fabric cloth, typically fiber bundles ranging from 3K to 12K and resin composition from 30 to 50 %. Typically used as planar reinforced structural components such as external fixator in medical applications.

3. Pyramid CC300 is long carbon fiber (1/2” or above) which requires a different blending process to incorporate PEEK resin such that it can be molded. Typically used as 3D reinforced structural components in medical and aerospace applications.

4. Pyramid CC400 is continuous unidirectional CF reinforced with cross ply. Typically used as reinforced panels in medical and aerospace applications.

From design perspective, CC200 and CC400 is really better for parts with uniform cross-sectional area such that machining will not breakdown the fiber length and can take advantage of continuous CF reinforcement. Typically this is bi-directional parts that has good resistance to compression, torsion or normal load to part surface. It will not perform well for shear (along surface) or tension normal to fiber direction. Note CC400 should actually be stronger and offer different type of lay up angles. CC200 does have different type of woven pattern and has a fabric/cloth look.

For complex parts, CC100 and 300 will offer better possibility for near net shape with varying cross-sectional areas.

Pyramid™ Unfilled PEEK Product Datasheets

Pyramid™ KD2000-G01 Unfilled PEEK Resin

Polyetheretherketone, Unfilled, Standard Flow

GENERAL

Form

Composition

Specific Gravity

Crystallinity, % maximum

Linear Mold Shrinkage, in/in

Moisture Absorption @24hr.

Melt Flow Index, g/10 min

MECHANICAL

Tensile Strength

Tensile Modulus

Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, notched

Izod, unnotched

Compressive Strength

Hardness

THERMAL

Melting Point

Glass Transition Temperature (Tg)

Flamability Rating

Heat Deflection Temperature (HDT) @ 264 psi

Thermal Conductivity

Coefficient of Linear Thermal Expansion

ELECTRICAL

Dielectric Strength

Dielectric Constant @ 1 KHz

Dielectric Factor @ 1 KHz

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
---
---
D792
---
D955
D570
D1238
D638
D638
D638
D790
D790
D256
D256
D695
D785
DSC/D3418
DSC/D3418
UL94
DMA/D648
F443/C177
D696/E831
D149
D150
D150
D257
D257
Pyramid™ KD2000-G01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
35%
0.012
<0.2
20 nominal
14 kpsi
508 kpsi
>60
25 kpsi
580 kpsi
1.7
no break
18 kpsi
M102
644°F
289°F
V-0
320°F
1.73 BTU-In/Hr-ft2-°F
33
480 V/mil
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-G01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
35%
0.012
<0.2
20 nominal
97 MPa
3.5 GPa
>60
172 MPa
4.0 GPa
0.91 J/cm
no break
124 MPa
Shore D88
340°C
143°C
V-0
160°C
0.25 W/m-K
59.4 µm/m-°C
18 KV/mm
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-G01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
Pyramid™ KD2000-J01 Unfilled PEEK Resin

Polyetheretherketone, Unfilled, Standard Flow

GENERAL

Form

Composition

Specific Gravity

Crystallinity, % maximum

Linear Mold Shrinkage, in/in

Moisture Absorption @ 24hr.

Melt Flow Index, g/10 min

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, notched

Izod, unnotched

Compressive Strength

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flamability Rating

Heat Deflection Temperature (HDT) @ 264psi

Thermal Conductivity

Coefficient of Linear Thermal Expansion

ELECTRICAL

Dielectric Strength

Dielectric Constant @ 1 KHz

Dielectric Factor @ 1 KHz

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
---
---
D792
---
D955
D570
D1238
D638
D638
D638
D790
D790
D256
D256
D695
D785
DSC/D3418
DSC/D3418
UL94
DMA/D648
F443/C177
D696/E831
D149
D150
D150
D257
D257
Pyramid™ KD2000-J01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
30%
0.012
<0.2
20 nominal
14 kpsi
510 kpsi
>40
23 kpsi
510 kpsi
1.8
no break
19 kpsi
M102
642°F
289°F
V-0
320°F
1.73 BTU-In/Hr-ft2-°F
26
480 V/mil
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-J01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
30%
0.012
<0.2
20 nominal
97 MPa
3.5 GPa
>40
159 MPa
3.5 GPa
0.96 J/cm
no break
131 MPa
Shore D88
339°C
143°C
V-0
160°C
0.25 W/m-K
47 µm/m-°C
18 KV/mm
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-J01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
Pyramid™ KD2000-J02 Unfilled PEEK Resin

Polyetheretherketone, Unfilled, Standard Flow

GENERAL

Form

Composition

Specific Gravity

Crystallinity, % maximum

Linear Mold Shrinkage, in/in

Moisture Absorption @ 24hr.

Melt Flow Index, g/10 min

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, notched

Izod, unnotched

Compressive Strength

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flamability Rating

Heat Deflection Temperature (HDT) @ 264psi

Thermal Conductivity

Coefficient of Linear Thermal Expansion

ELECTRICAL

Dielectric Strength

Dielectric Constant @ 1 KHz

Dielectric Factor @ 1 KHz

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
---
---
D792
---
D955
D570
D1238
D638
D638
D638
D790
D790
D256
D256
D695
D785
DSC/D3418
DSC/D3418
UL94
DMA/D648
F443/C177
D696/E831
D149
D150
D150
D257
D257
Pyramid™ KD2000-J02 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
30%
0.012
<0.2
20 nominal
14 kpsi
510 kpsi
>30
22 kpsi
510 kpsi
1.5
no break
18 kpsi
M102
642°F
289°F
V-0
320°F
1.73 BTU-In/Hr-ft2-°F
26
480 V/mil
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-J02 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
30%
0.012
<0.2
20 nominal
97 MPa
3.5 GPa
>30
152 MPa
3.5 GPa
0.8 J/cm
no break
124 MPa
Shore D88
339°C
143°C
V-0
160°C
0.25 W/m-K
47 µm/m-°C
18 KV/mm
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-J02 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
Pyramid™ KD2000-R01 Unfilled PEEK Resin

Polyetheretherketone, Unfilled, Standard Flow

GENERAL

Form

Composition

Specific Gravity

Crystallinity, % maximum

Linear Mold Shrinkage, in/in

Moisture Absorption @ 24hr.

Melt Flow Index, g/10 min

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, notched

Izod, unnotched

Compressive Strength

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flamability Rating

Heat Deflection Temperature (HDT) @ 264psi

Thermal Conductivity

Coefficient of Linear Thermal Expansion

ELECTRICAL

Dielectric Strength

Dielectric Constant @ 1 KHz

Dielectric Factor @ 1 KHz

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
---
---
D792
---
D955
D570
D1238
D638
D638
D638
D790
D790
D256
D256
D695
D785
DSC/D3418
DSC/D3418
UL94
DMA/D648
F443/C177
D696/E831
D149
D150
D150
D257
D257
Pyramid™ KD2000-R01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
35%
0.012
<0.2
20 nominal
14 kpsi
510 kpsi
>40
25 kpsi
580 kpsi
1.7
no break
18 kpsi
M102
644°F
289°F
V-0
320°F
1.73 BTU-In/Hr-ft2-°F
26
480 V/mil
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-R01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
30%
0.012
<0.2
20 nominal
97 MPa
3.5 GPa
>40
172 MPa
4.0 GPa
0.91 J/cm
no break
124 MPa
Shore D88
340°C
143°C
V-0
160°C
0.25 W/m-K
47 µm/m-°C
18 KV/mm
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-R01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
Pyramid™ KD2000-R02 Unfilled PEEK Resin

Polyetheretherketone, Unfilled, Standard Flow

GENERAL

Form

Composition

Specific Gravity

Crystallinity, % maximum

Linear Mold Shrinkage, in/in

Moisture Absorption @ 24hr.

Melt Flow Index, g/10 min

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, notched

Izod, unnotched

Compressive Strength

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flamability Rating

Heat Deflection Temperature (HDT) @ 264psi

Thermal Conductivity

Coefficient of Linear Thermal Expansion

ELECTRICAL

Dielectric Strength

Dielectric Constant @ 1 KHz

Dielectric Factor @ 1 KHz

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
---
---
D792
---
D955
D570
D1238
D638
D638
D638
D790
D790
D256
D256
D695
D785
DSC/D3418
DSC/D3418
UL94
DMA/D648
F443/C177
D696/E831
D149
D150
D150
D257
D257
Pyramid™ KD2000-R01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
35%
0.012
<0.2
20 nominal
14 kpsi
510 kpsi
>40
25 kpsi
580 kpsi
1.7
no break
18 kpsi
M102
644°F
289°F
V-0
320°F
1.73 BTU-In/Hr-ft2-°F
26
480 V/mil
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-R01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
Pellets (tan)
Neat Resin
1.3 g/ml
30%
0.012
<0.2
20 nominal
97 MPa
3.5 GPa
>40
172 MPa
4.0 GPa
0.91 J/cm
no break
124 MPa
Shore D88
340°C
143°C
V-0
160°C
0.25 W/m-K
47 µm/m-°C
18 KV/mm
3.3
0.004
1 Ohm-cm x 1016
2 Ohm-cm x 1016
Pyramid™ KD2000-R01 Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
Pyramid™ KD2000 Unfilled PEEK CAM™ Molded

Polyetheretherketone (PEEK) Tube

GENERAL

Specific Gravity

Moisture Absorption @ 24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

THERMAL

Melting Point (Tm)

Coefficient of Linear Thermal Expansion

Heat Deflection Temperature (HDT) @ 264psi

Flexural Modulus

Flammability

Flammability Rating (1.6 mm)

Oxygen Index (3.2 mm)

ELECTRICAL

Dielectric Strength

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
DSC
D696
DMA
D3418
UL94
D2863
D149
D257
D257
Pyramid™ KD2000 CAM™ Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
1.3 g/ml
0.2%
15.2 kpsi
0.5 kpsi
>30
20 kpsi
0.5 Mpsi
644°F
2.6
302
289
V-0
38%
530 V/mil
1 Ohm-cm x 1014
1 Ohm-cm x 1014
Pyramid™ KD2000 CAM™ Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
1.3 g/ml
0.2%
105 MPa
3.4 GPa
>30
137 MPa
3.4 GPa
340°C
4.7 µm/m-°C
150°C
143°C
V-0
38%
21 KV/mm
1 Ohm-cm x 1014
1 Ohm-cm x 1014
Pyramid™ KD2000 CAM™ Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
Pyramid™ KD2000 Unfilled PEEK Injection Molded Shape

Polyetheretherketone (PEEK) Tube

GENERAL

Specific Gravity

Moisture Absorption @ 24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

THERMAL

Melting Point (Tm)

Coefficient of Linear Thermal Expansion

Heat Deflection Temperature (HDT) @ 264psi

Flexural Modulus

Flammability

Flammability Rating (1.6 mm)

Oxygen Index (3.2 mm)

ELECTRICAL

Dielectric Strength

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
DSC
D696
DMA
D3418
UL94
D2863
D149
D257
D257
Pyramid™ KD2000 Injection Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
1.3 g/ml
0.5%
14 kpsi
0.5 kpsi
30%
21 kpsi
0.5 Mpsi
644°F
2.6
302
289
V-0
38%
530 V/mil
1 Ohm-cm x 1014
1 Ohm-cm x 1014
Pyramid™ KD2000 Injection Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
1.3 g/ml
0.2%
105 MPa
3.4 GPa
30%
145 MPa
3.4 GPa
340°C
4.7 µm/m-°C
150°C
143°C
V-0
38%
21 KV/mm
1 Ohm-cm x 1014
1 Ohm-cm x 1014
Pyramid™ KD2000 Injection Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
Pyramid™ KD2000 Unfilled PEEK Compression Molded Shape

Polyetheretherketone (PEEK) Tube

GENERAL

Specific Gravity

Moisture Absorption @ 24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

THERMAL

Melting Point (Tm)

Coefficient of Linear Thermal Expansion

Heat Deflection Temperature (HDT) @ 264psi

Flexural Modulus

Flammability

Flammability Rating (1.6 mm)

Oxygen Index (3.2 mm)

ELECTRICAL

Dielectric Strength

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
DSC
D696
DMA
D3418
UL94
D2863
D149
D257
D257
Pyramid™ KD2000 Compression Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
ENGLISH VALUE
1.3 g/ml
0.2%
14.9 kpsi
0.45 Mpsi
10%
25 kpsi
0.45 Mpsi
644°F
2.6
302
289
V-0
38%
530 V/mil
1 Ohm-cm x 1014
1 Ohm-cm x 1014
Pyramid™ KD2000 Compression Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)
METRIC VALUE
1.3 g/ml
0.2%
103 MPa
3.1 GPa
10%
172 MPa
3.1 GPa
340°C
4.7 µm/m-°C
150°C
143°C
V-0
38%
21 KV/mm
1 Ohm-cm x 1014
1 Ohm-cm x 1014
Pyramid™ KD2000 Compression Molded Product Properties Datasheet (PDF)
Unfilled PEEK MSDS (PDF)

Pyramid™ Reinforced PEEK Product Datasheets

Pyramid™ KD2150 30% Glass Fiber Filled PEEK Pellets

PEEK with 30% Glass Fiber

GENERAL

Form

Composition (Polyetheretherketone)

Filler Content (Nominal value)

Density

Linear Mold Shrinkage

Moisture Absorption @24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

Hardness

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
D256
D2240/D792
Pyramid™ KD2150 30% Glass Fiber Filled PEEK Pellets Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (tan)
PEEK
30% Glass Fiber
0.055 lb/in3
0.008 in/in
0.1%
18 kpsi
1.17 Mpsi
2.8%
28 kpsi
1.19 Mpsi
1.0 ft-lb/in @ 1/8 in
M101 Rockwell M
Pyramid™ KD2150 30% Glass Fiber Filled PEEK Pellets Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
METRIC VALUE
Pellets (tan)
PEEK
30% Glass Fiber
1.53 g/ml
0.008 cm/cm
0.1%
120 MPa
8.1 GPa
2.8%
192 MPa
8.2 GPa
0.7 J/cm
D90 Shore D
Pyramid™ KD2150 30% Glass Fiber Filled PEEK Pellets Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
Pyramid™ KD2152 30% Glass Fiber Filled PEEK Injection Molding Grade Pellets

PEEK with 30% Glass Fiber

GENERAL

Form

Composition (Polyetheretherketone)

Filler Content (Nominal value)

Density

Linear Mold Shrinkage

Moisture Absorption @24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

Hardness

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
D256
D2240/D792
Pyramid™ KD2152 30% Glass Fiber Filled PEEK Injection Molding Grade Pellets Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (tan)
PEEK
30% Glass Fiber
0.055 lb/in3
0.008 in/in
0.1%
18 kpsi
1.17 Mpsi
3.1%
28 kpsi
1.19 Mpsi
1.0 ft-lb/in @ 1/8 in
M101 Rockwell M
Pyramid™ KD2152 30% Glass Fiber Filled PEEK Injection Molding Grade Pellets Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
METRIC VALUE
Pellets (tan)
PEEK
30% Glass Fiber
1.53 g/ml
0.008 cm/cm
0.1%
120 MPa
8.1 GPa
3.1%
192 MPa
8.2 GPa
0.7 J/cm
D90 Shore D
Pyramid™ KD2152 30% Glass Fiber Filled PEEK Injection Molding Grade Pellets Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
Pyramid™ KD2250-NT 30% Glass Fiber Filled PEEK

PEEK with 30% Glass Fiber

GENERAL

Filler Content (Nominal value)

Specific Gravity

Linear Mold Shrinkage

Moisture Absorption @24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Compressive Strength

Izod, Notched

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Coefficient of Linear Thermal Expansion

Heat Deflection Temperature (HDT) @ 264psi

Thermal Conductivity

Flammability Rating

OTHER

Dynamic Coefficient of Friction

Poisson’s Ratio

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
D695
D256
D785
DSC
D3418
D696
DMA/D648
C177
UL94
D1894
Pyramid™ KD2250-NT 30% Glass Fiber Filled PEEK Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
ENGLISH VALUE
30%
1.40 g/ml
0.003 in/in
0.06%
33.6 kpsi
3.3 Mpsi
2%
56.3 kpsi
3.0 Mpsi
34.8 kpsi
1.1 ft-lb/in @ 1/8 in
107M Rockwell M
651°F
289°F
7.7
599°F
38 Btu-in/hr-ft2 - °F
V-0
0.16
0.44
Pyramid™ KD2250-NT 30% Glass Fiber Filled PEEK Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
METRIC VALUE
30%
1.40 g/ml
0.003 in/in
0.06%
232 MPa
23 GPa
2%
388 MPa
21 GPa
240 MPa
58.7 J/m
124R
344°C
143°C
14 µm/m-°C
315°C
0.92 W/m-K
V-0
0.16
0.44
Pyramid™ KD2250-NT 30% Glass Fiber Filled PEEK Product Properties Datasheet (PDF)
Glass Filled PEEK MSDS (PDF)
Pyramid™ KD2450-NT 30% Ceramic Filled PEEK

PEEK with 30% Ceramic Filler

GENERAL

Form

Composition

Filler Content

Density

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flammability Rating

Heat Deflection Temperature (HDT) @ 264psi

Coefficient of Linear Thermal Expansion

ELECTRICAL

Dielectrical Strength

Dissipation Factor @ 1 MHz

Volume Resistivity

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D638
D638
D638
D790
D790
D256
DSC
DSC
UL94
D648
D696
D149
D150
D257
D257
Pyramid™ KD2450-NT 30% Ceramic Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND -Ceramic Filled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets
Ceramic Filled PEEK
30%
0.054 lb/in3
11.5 kpsi
0.6 Mpsi
>10%
22 kpsi
0.6 Mpsi
1 ft-lb/in @ 1/8 in
645°F
290°F
>500
2 x 10-5
400 V/mil
0.005
1 Ohm-cm x 1015
1 Ohm/sq x 1013
Pyramid™ KD2450-NT 30% Ceramic Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND -Ceramic Filled PEEK MSDS (PDF)
METRIC VALUE
Pellets
Ceramic Filled PEEK
30%
1.5 g/ml
80 MPa
4.4 GPa
>10%
155 MPa
4.4 GPa
53 J/m
341°C
143°C
>260°C
3.6 x 10-5 µm/m-°C
15 KV/mm
0.005
1 Ohm-cm x 1015
1 Ohm/sq x 1013
Pyramid™ KD2450-NT 30% Ceramic Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND -Ceramic Filled PEEK MSDS (PDF)
Pyramid™ KD2440 Ceramic Filled ESD PEEK

Ceramic filled ESD PEEK for Test Sockets

GENERAL

Composition

Density

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Heat Deflection Temperature (HDT) @ 264psi

Coefficient of Linear Thermal Expansion

ELECTRICAL

Volume Resistivity, Ohm-cm

Surface Resistivity, Ohm/sq

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D638
D638
D638
D790
D790
D256
DSC
DSC
D648
D696
D257
D257
Pyramid™ KD2440 Ceramic Filled ESD PEEK Product Properties Datasheet (PDF)
NOT FOUND -Ceramic Filled PEEK MSDS (PDF)
ENGLISH VALUE
Ceramic Filled ESD PEEK
0.055 lb/in3
13.8 kpsi
0.67 Mpsi
>10%
24 kpsi
0.65 Mpsi
1 ft-lb/in @ 1/8 in
645°F
290°F
>500
2 x 10-5
1e9 – 1e12
1e9 – 1e12
Pyramid™ KD2440 Ceramic Filled ESD PEEK Product Properties Datasheet (PDF)
NOT FOUND -Ceramic Filled PEEK MSDS (PDF)
METRIC VALUE
Ceramic Filled ESD PEEK
1.5 g/cm3
95 MPa
5 GPa
>10%
165 MPa
4.8 GPa
53 J/cm
341°C
143°C
>260°C
3.6 x 10-5 µm/m-°C
1e9 – 1e12
1e9 – 1e12
Pyramid™ KD2440 Ceramic Filled ESD PEEK Product Properties Datasheet (PDF)
NOT FOUND -Ceramic Filled PEEK MSDS (PDF)
Pyramid™ KD2520-NT 15% PTFE Filled PEEK

PEEK Lubricated, Standard Flow

GENERAL

Form

Composition

Filler Content (Nominal value)

Specific Gravity

Shrinkage (MD/TD)

Moisture Absorption @24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flammability Rating

Heat Deflection Temperature (HDT) @ 264psi

OTHER

Kinetic Coefficients of Friction

Static Coefficients of Friction

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D955
D570
D638
D638
D638
D790
D790
D256
D2240
DSC
DSC
UL94
D648
D1894
D1894
Pyramid™ KD2520-NT 15% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (Gray)
PTFE Filled PEEK
15%
1.39
0.010/0.020 in/in
0.1%
12 kpsi
0.5 Mpsi
18%
21 kpsi
0.52 Mpsi
0.8 ft-lb/in @ 1/8 in
85 Shore D
650°F
290°F
V-0
340°F
0.11
0.11
Pyramid™ KD2520-NT 15% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
METRIC VALUE
Pellets (Gray)
PTFE Filled PEEK
15%
Pyramid™ KD2520-NT 15% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
Pyramid™ KD2530-NT 20% PTFE Filled PEEK

PEEK Lubricated, Standard Flow

GENERAL

Form

Composition

Filler Content (Nominal value)

Specific Gravity

Shrinkage (MD/TD)

Moisture Absorption @24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flammability Rating

Heat Deflection Temperature (HDT) @ 264psi

OTHER

Kinetic Coefficients of Friction

Static Coefficients of Friction

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D955
D570
D638
D638
D638
D790
D790
D256
D2240
DSC
DSC
UL94
D648
D1894
D1894
Pyramid™ KD2530-NT 20% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (Gray)
PTFE Filled PEEK
20%
1.42
0.1%
11.5 kpsi
0.46 Mpsi
15%
20 kpsi
0.5 Mpsi
0.8 ft-lb/in @ 1/8 in
84 Shore D
650°F
290°F
V-0
340°F
0.1
0.1
Pyramid™ KD2530-NT 20% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
METRIC VALUE
Pellets (Gray)
PTFE Filled PEEK
20%
Pyramid™ KD2530-NT 20% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
Pyramid™ KD2540-NT 25% PTFE Filled PEEK

PEEK Lubricated, Standard Flow

GENERAL

Form

Composition

Filler Content (Nominal value)

Specific Gravity

Shrinkage (MD/TD)

Moisture Absorption @24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flammability Rating

Heat Deflection Temperature (HDT) @ 264psi

OTHER

Kinetic Coefficients of Friction

Static Coefficients of Friction

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D955
D570
D638
D638
D638
D790
D790
D256
D2240
DSC
DSC
UL94
D648
D1894
D1894
Pyramid™ KD2540-NT 25% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (Gray)
PTFE Filled PEEK
25%
1.44
0.015/0.023 in/in
0.1%
11.2 kpsi
0.46 Mpsi
10%
19 kpsi
0.48 Mpsi
0.6 ft-lb/in @ 1/8 in
82 Shore D
650°F
290°F
V-0
340°F
0.08
0.1
Pyramid™ KD2540-NT 25% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
METRIC VALUE
Pellets (Gray)
PTFE Filled PEEK
25%
Pyramid™ KD2540-NT 25% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
Pyramid™ KD2550-NT 30% PTFE Filled PEEK

PEEK Lubricated, Standard Flow

GENERAL

Form

Composition

Filler Content (Nominal value)

Specific Gravity

Shrinkage (MD/TD)

Moisture Absorption @24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Izod, Notched

Hardness

THERMAL

Melting Point (Tm)

Glass Transition Temperature (Tg)

Flammability Rating

Heat Deflection Temperature (HDT) @ 264psi

OTHER

Kinetic Coefficients of Friction

Static Coefficients of Friction

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D955
D570
D638
D638
D638
D790
D790
D256
D2240
DSC
DSC
UL94
D648
D1894
D1894
Pyramid™ KD2550-NT 30% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
ENGLISH VALUE
Pellets (Gray)
PTFE Filled PEEK
30%
1.45
0.1%
10.5 kpsi
0.4 Mpsi
4%
18 kpsi
0.47 Mpsi
0.6 ft-lb/in @ 1/8 in
81 Shore D
650°F
290°F
V-0
340°F
0.08
0.1
Pyramid™ KD2550-NT 30% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
METRIC VALUE
Pellets (Gray)
PTFE Filled PEEK
30%
Pyramid™ KD2550-NT 30% PTFE Filled PEEK Product Properties Datasheet (PDF)
NOT FOUND - PTFE Filled PEEK MSDS (PDF)
Pyramid™ KD2219 Wear Grade PEEK

PEEK Wear Grade

GENERAL

Density

Filler Content (Nominal value)

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Flexural Strength

Flexural Modulus

Tensile Elongation (Break)

Izod, Notched

THERMAL

Heat Deflection Temperature (HDT) @ 264psi

Glass Transition Temperature (Tg)

Melting Point (Tm)

OTHER

Dynamic Coefficient of Friction

Static Coefficient of Friction

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D638
D638
D790
D790
D638
D256
D648
DSC
DSC
D1894
D1894
Pyramid™ KD2219 Wear Grade PEEK Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
ENGLISH VALUE
0.053 lb/in3
30%
23.2 kpsi
1.3 Mpsi
32 kpsi
1.3 Mpsi
2.5%
1.2 ft-lb/in @ 1/8 in
580°F
289°F
644°F
0.11
0.11
Pyramid™ KD2219 Wear Grade PEEK Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
METRIC VALUE
1.45 g/cm3
30%
160 MPa
9.0 GPa
220 MPa
13 GPa
2.5%
0.64 J/cm
300°C
143°C
340°C
0.11
0.11
Pyramid™ KD2219 Wear Grade PEEK Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
Pyramid™ KD4219 High Temperature Wear Resistant PEEK - Resin Compound

Ultra-High Performance Thermoplastic Polymer

GENERAL

Specific Gravity

Color

Composition

Moisture Absorption @ 24hr.

Flammability Rating

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Compressive Strength

Shear Strength

Izod, Notched @ 1/8"

Izod, Un-Notched @ 1/8"

Hardness, Rockwell

Hardness, Shore D

Limiting PV (4:1 safety factor)

Static Coefficient of Friction (dry vs. steel)

Dynamic Coefficient of Friction (dry vs. steel)

THERMAL

Glass Transition Temperature - Tg

Heat Deflection Temperature (HDT) @ 264psi

Melting Point (Tm)

Coef. of Linear Thermal Expansion -40°F – 300°F / 40ºC – 150ºC

Thermal Conductivity

ELECTRICAL

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
UL 94
D638
D638
D638
D790
D790
D695
D732
D256
D256
D785
D2240
PTM
PTM
DSC
D648
DSC
TMA
C177
D257
Pyramid™ KD4219 High Temperature Wear Resistant PEEK Resin Compound Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
ENGLISH VALUE
1.46
Black
PEEK / Carbon Fibers / Proprietary Lubricants
0.04%
V-0
25 kpsi
1,800 kpsi
2%
36 kpsi
1,800 kpsi
32 kpsi
20 kpsi
1.0 ft-lb/in
12 ft-lb/in
M90
D83
32,000 ft.lbs.ft./in.2min.
0.25
0.17
320°F
500°F
680°F
25 µin/in-°F
1.75 BTU-in/hr-ft2-°F
<1 x 108Ohm/sq
Pyramid™ KD4219 High Temperature Wear Resistant PEEK Resin Compound Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
METRIC VALUE
1.46
Black
PEEK / Carbon Fibers / Proprietary Lubricants
0.04%
V-0
172 MPa
12,400 MPa
2%
248 MPa
12,400 MPa
220 MPa
138 MPa
0.53 J/cm
6.7 J/cm
M90
D83
32,000 ft.lbs.ft./in.2min.
0.25
0.17
160°C
260°C
360°C
45 µm/m-°C
0.25 W/m-K
<1 x 108Ohm/sq
Pyramid™ KD4219 High Temperature Wear Resistant PEEK Resin Compound Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
Pyramid™ KD4219 High Temperature Wear Resistant PEEK - Stock Shapes

Ultra-High Performance Thermoplastic Polymer

GENERAL

Specific Gravity

Color

Composition

Moisture Absorption @ 24hr.

Flammability @ 1/8” (estimated)

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Compressive Strength

Shear Strength

Izod, Notched @ 1/8"

Izod, Un-Notched @ 1/8"

Hardness, Rockwell

Hardness, Shore D

Limiting PV (4:1 safety factor)

Static Coefficient of Friction (dry vs. steel)

Dynamic Coefficient of Friction (dry vs. steel)

THERMAL

Glass Transition Temperature - Tg

Heat Deflection Temperature (HDT) @ 264psi

Melting Point (Tm)

Coef. of Linear Thermal Expansion -40°F – 300°F / 40ºC – 150ºC

Thermal Conductivity

ELECTRICAL

Surface Resistivity

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
UL 94
D638
D638
D638
D790
D790
D695
D732
D256
D256
D785
D2240
PTM
PTM
DSC
D648
DSC
TMA
C177
D257
Pyramid™ KD4219 High Temperature Wear Resistant PEEK Stock Shapes Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
ENGLISH VALUE
1.46
Black
PEEK / Carbon Fibers / Proprietary Lubricants
0.04%
V-0
18 kpsi
1,400 kpsi
1.5%
28 kpsi
1,500 kpsi
28 kpsi
14 kpsi
0.8 ft-lb/in
5 ft-lb/in
M92
D84
35,000 ft.lbs.ft./in.2min.
0.25
0.17
320°F
500°F
680°F
25 µin/in-°F
1.75 BTU-in/hr-ft2-°F
<1 x 108Ohm/sq
Pyramid™ KD4219 High Temperature Wear Resistant PEEK Stock Shapes Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
METRIC VALUE
1.46
Black
PEEK / Carbon Fibers / Proprietary Lubricants
0.04%
V-0
124 MPa
9,700 MPa
1.5%
193 MPa
10,300 MPa
193 MPa
97 MPa
0.42 J/cm
2.6 J/cm
M92
D84
35,000 ft.lbs.ft./in.2min.
0.25
0.17
160°C
260°C
360°C
45 µm/m-°C
0.25 W/m-K
<1 x 108Ohm/sq
Pyramid™ KD4219 High Temperature Wear Resistant PEEK Stock Shapes Product Properties Datasheet (PDF)
Wear Grade PEEK MSDS (PDF)
Pyramid™ KD210SG Seal Grade PEEK

Polyaryletherketone-Fluropolymer compound

GENERAL

Density

Moisture Absorption @ 24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

THERMAL

Melting Point (Tm)

Glass Transition Temperature - Tg

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
DSC
DSC
Pyramid™ KD210SG Seal Grade PEEK Product Properties Datasheet (PDF)
NOT FOUND - Seal Grade PEEK MSDS (PDF)
ENGLISH VALUE
0.0473 lb/in3
0.05%
12.2 Kpsi
480 Kpsi
>100%
120 Kpsi
500 Kpsi
645°F
193°F
Pyramid™ KD210SG Seal Grade PEEK Product Properties Datasheet (PDF)
NOT FOUND - Seal Grade PEEK MSDS (PDF)
METRIC VALUE
1.31 g/ml
0.05%
84 MPa
3.3 GPa
>100%
82 MPa
3.4 GPa
340°C
145°C
Pyramid™ KD210SG Seal Grade PEEK Product Properties Datasheet (PDF)
NOT FOUND - Seal Grade PEEK MSDS (PDF)

Pyramid™ CC PEEK Product Datasheets

Pyramid™ CC100 60% Chopped Carbon Fabric/Tape PEEK

PEEK with 60% Chopped Carbon Fabric/Tape

GENERAL

Form

Composition (base resin)

Reinforcement

Filler Content

Color

Density

Moisture Absorption @ 24hr.

MECHANICAL

Tensile Strength (Break)

Tensile Modulus

Tensile Elongation (Break)

Flexural Strength

Flexural Modulus

Compressive Strength

Compressive Modulus

Hardness

Izod, Notched @ 1/8"

THERMAL

Melting Point (Tm)

Glass Transition Temperature - Tg

Flammability Rating

Heat Deflection Temperature (HDT) @ 264psi

ELECTRICAL

Volume Resistivity, Ohm-cm

Surface Resistivity, Ohm-sq

Datasheet Download (PDF)

MSDS Download (PDF)

ASTM METHOD
D792
D570
D638
D638
D638
D790
D790
D695
D695
D2240
D256
DSC
DSC
UL 94
D648
D257
D257
Pyramid™ CC100 60% Chopped Carbon Fabric/Tape PEEK Product Properties Datasheet (PDF)
NOT FOUND - Chopped Carbon Fabric/Tape PEEK MSDS (PDF)
ENGLISH VALUE
Compression Molded Shape
PEEK
Chopped Carbon Fiber/Tape
60% nominal
Gray/Black
0.054 lb/in3
0.05%
45 Kpsi
5.2 Mpsi
1.0%
48 Kpsi
4.9 Mpsi
40 Kpsi
3.6 Mpsi
M110 Rockwell M
2.1 ft-lb/in
644°F
289°F
V-0
>580°F
<100
<100
Pyramid™ CC100 60% Chopped Carbon Fabric/Tape PEEK Product Properties Datasheet (PDF)
NOT FOUND - Chopped Carbon Fabric/Tape PEEK MSDS (PDF)
METRIC VALUE
Compression Molded Shape
PEEK
Chopped Carbon Fiber/Tape
60% nominal
Gray/Black
1.5 g/cm3
0.05%
310 MPa
36 GPa
1.0%
330 MPa
34 GPa
275 MPa
25 GPa
D96 Shore D
1.1 J/cm
340°C
143°C
V-0
>300°C
<100
<100
Pyramid™ CC100 60% Chopped Carbon Fabric/Tape PEEK Product Properties Datasheet (PDF)
NOT FOUND - Chopped Carbon Fabric/Tape PEEK MSDS (PDF)

We Provide Solutions

Regardless of the industry or end-use, we have the expertise to quickly and economically create the ideal polymer for the job.

Polymics, Ltd. #1 Best High Temperature Polymers and Composites

Polymics,® Ltd. is the only polymers company in the world that has the expertise and manufacturing capabilities to take customers from high performance thermoplastic material development to final part molding and assembly. Our in-house polymers engineering staff provides our customers with true one-stop “Problem to Finished Part Solutions” by working on their individual problem from start to finish.

Celazole® is a registered trademark of PBI Performance Products, Inc.

Shale Gas Innovation Award - #1 Best High Temperature Polymers and Composites
Polymics ISO Certificate
Polymics Ltd. #1 Best High Temperature Polymers and Composites

Corporate Headquarters

2215 High Tech Road,
State College, PA 16803

Tel: 814.357.5860
Fax: 814.357.5863

Email: info@polymics.com

Polymics Ltd. #1 Best High Temperature Polymers and Composites

U.S. Sales Office

8902 FM 2920, Suite 200
Spring, TX 77579

Tel: 832.672.7181
Tel: 832.672.7187

Email: info@polymics.com

Polymics Ltd. #1 Best High Temperature Polymers and Composites

Asian Pacific

No.272, Huakang St.
Bade Dist., Taoyuan
Taiwan, 33464

Tel: 886.3.377.0518
Fax: 886.3.367.2115

Email: info@polymics.com

This information and all further technical advice are based Polymics’ present knowledge and experience. However, neither Polymics Ltd nor any of its affiliates makes any warranty, express or implied, including merchantability or fitness for use, or accepts any liability in connection with this information or its use. This information is for use by technically skilled persons at their own discretion and risk and does not relate to the use of this product in combination with any other substance or any other process. This is not a license under any patent or other proprietary right. The use of this product resides on the determination of the customer not Polymics Ltd. The customer must determine suitability of any information or material for any contemplated use, the manner of use and whether any patents are infringed. This information gives typical properties only and is not to be used for specification purposes. Polymics reserves the right to make additions, deletions, or modifications to the information at any time without prior notification.